Alginate/PVA Polymer Electrolyte Membrane Modified by Hydrophilic Montmorillonite for Structure and Selectivity Enhancement for DMFC Application
Nafion is a commercial membrane that is widely used in direct methanol fuel cells (DMFC) but has critical constraints such as being expensive and having high methanol crossover. Efforts to find alternative membranes are actively being carried out, including in this study, which looks at producing a Sodium Alginate/Poly (Vinyl Alcohol) (SA/PVA) blended membrane with modification by montmorillonite (MMT) as an inorganic filler. The content of MMT in SA/PVA-based membranes varied in the range of 2.0–20 wt% according to the solvent casting method implemented. The presence of MMT was seen to be most optimal at a content of 10 wt%, achieving the highest proton conductivity and the lowest methanol uptake of 9.38 mScm−1 and 89.28% at ambient temperature, respectively. The good thermal stability, optimum water absorption, and low methanol uptake of the SA/PVA-MMT membrane were achieved with the presence of MMT due to the strong electrostatic attraction between H+, H3O+, and −OH ions of the sodium alginate and PVA polymer matrices. The homogeneous dispersion of MMT at 10 wt% and the hydrophilic properties possessed by MMT contribute to an efficient proton transport channel in SA/PVA-MMT membranes. The increase in MMT content makes the membrane more hydrophilic. This shows that the loading of 10 wt% MMT is very helpful from the point of view of sufficient water intake to activate proton transfer. Thus, the membrane produced in this study has great potential as an alternative membrane with a much cheaper cost and competent future performance.
» Author: Maryam Taufiq Musa
» Reference: doi: 10.3390/polym15122590
» Publication Date: 06/06/2023
This project has received funding from the European Union's Horizon 2020 research and innovation programme under grant agreement Nº 768737