The Study of Crystallization Behavior, Microcellular Structure and Thermal Properties of Glass-Fiber/Polycarbonate Composites

Polycarbonate (PC) foam is a versatile material with excellent properties, but its low thermal stability limits its application in high-temperature environments. The aim of this study was to improve the thermal stability of PC foam by adding glass fibers (GF) and to investigate the effect of GF on PC crystallization behavior and PC foam cell morphology. This study was motivated by the need to improve the performance of PC foams in various industries, such as construction, automotive, and medical. To achieve this goal, PC/GF composites were prepared by extrusion, and PC/GF composite foams were produced using a batch foaming process with supercritical carbon dioxide (SC-CO2) as the blowing agent. The results showed that the addition of GF accelerated the SC-CO2-induced crystallization stability of PC and significantly increased the cell density to 4.6 cells/cm3. In addition, the thermal stability of PC/GF foam was improved, with a significant increase in the residual carbon rate at 700 °C and a lower weight loss rate than PC matrix. Overall, this study highlights the potential of GF as a PC foam reinforcement and its effect on thermal and structural properties, providing guidance for industrial production and applications.

» Author: Xinchao Wang

» Reference: doi: 10.3390/polym15061546

» Publication Date: 21/03/2023

» More Information

« Go to Technological Watch





This project has received funding from the European Union's Horizon 2020 research and innovation programme under grant agreement Nº 768737


                   




AIMPLAS, Plastics Technology Centre

+34 96 136 60 40