Ionic Transport Properties of P2O5-SiO2 Glassy Protonic Composites Doped with Polymer and Inorganic Titanium-based Fillers
This paper is focused on the determination of the physicochemical properties of a composite inorganic–organic modified membrane. The electrical conductivity of a family of glassy protonic electrolytes defined by the general formula (P2O5)x(SiO2)y, where x/y is 3/7 are studied by Alternating Current electrochemical impedance spectroscopy (AC EIS) method. The reference glass was doped with polymeric additives—poly(ethylene oxide) (PEO) and poly(vinyl alcohol) (PVA), and additionally with a titanium-oxide-based filler. Special attention was paid to determination of the transport properties of the materials thus modified in relation to the charge transfer phenomena occurring within them. The electrical conductivities of the ‘dry’ material ranged from 10−4 to 10−9 S/cm, whereas for ‘wet’ samples the values were ~10−3 S/cm. The additives also modified the pore space of the samples. The pore distribution and specific surface of the modified glassy systems exhibited variation with changes in electrolyte chemical composition. The mechanical properties of the samples were also examined. The Young’s modulus and Poisson’s ratio were determined by the continuous wave technique (CWT). Based on analysis of the dispersion of the dielectric losses, it was found that the composite samples exhibit mixed-type proton mobility with contributions related to both the bulk of the material and the surface of the pore space.
» Author: Maciej Siekierski
» Reference: doi: 10.3390/ma13133004
» Publication Date: 06/07/2020
This project has received funding from the European Union's Horizon 2020 research and innovation programme under grant agreement Nº 768737